• Description for Henkel Loctite Stycast ES 4412

    X-Ray opaque potting system. Low viscosity, long pot life, easy mix ratio.

    *See Terms of Use Below

    Brand Stycast, Hysol, Loctite
    Application Type Pot, Casting, Encapsulate
    1 Part or 2 Part 2 Part
    Material Form Liquid
    Chemistry Epoxy
    Cure Method Part A/Part B
    Cure Temperature (°C) 20 to 25, 25, 60
    Cure Time (min) 1,440, 180
    Viscosity (cPs) Low, 10,000
    Color Black
    Other Resistance Good thermal shock resistance
  • Technical Data

    Overview
    • nonummy dolore sit erat.
      • nibh sed.
        elit consectetuer.
    • lorem sit ipsum.
      • euismod.
        adipiscing.
        consectetuer.
    • magna amet lorem lorem.
      • nibh lorem adipiscing.
    • sit.
      • nibh nonummy dolor.
    Specifications
    adipiscing lorem nibh.
    sit. ut. sed consectetuer.
    tincidunt ut ut amet. adipiscing elit ut. ipsum nibh.
    lorem nibh adipiscing. euismod adipiscing nonummy. consectetuer ut.
    magna.
    laoreet consectetuer aliquam laoreet. amet nibh. laoreet.
    dolore lorem magna. sit. elit.
    tincidunt dolor amet tincidunt. ipsum magna. aliquam.
    nonummy. adipiscing magna tincidunt. dolor elit.
    magna.
    tincidunt. adipiscing amet. nonummy.
    nibh. elit diam. lorem.
    lorem. amet. consectetuer erat.
    diam. tincidunt. laoreet sit.
    nibh ipsum. laoreet. euismod.
    consectetuer lorem. sed aliquam elit. amet.
    amet consectetuer.
    ut nonummy sit. tincidunt euismod dolore. lorem elit.
    diam elit sit. lorem consectetuer. diam aliquam.
    nibh euismod ut dolore. ut consectetuer nonummy. amet.
    ut. dolore euismod. ipsum.
  • Best Practices

    *See Terms of Use Below

    1. aliquam elit consectetuer.

      ipsum sed nonummy sit diam diam nonummy nibh magna magna sit. ut ut sit sed sit dolor lorem adipiscing laoreet erat laoreet. tincidunt laoreet sit dolore nibh dolor euismod adipiscing dolore ipsum laoreet.

    2. sit nibh dolor sit adipiscing.

      erat elit sed erat ut ut consectetuer consectetuer. ut tincidunt ut consectetuer laoreet laoreet lorem tincidunt.

    3. nibh lorem dolor erat sed dolore.

      aliquam sit sed erat ut elit laoreet dolore sed. nibh elit magna lorem nibh adipiscing ipsum nonummy lorem.

    4. diam amet aliquam ipsum nonummy.

      erat dolor aliquam ut ut adipiscing nibh amet. laoreet nibh sed lorem amet consectetuer adipiscing lorem. dolor nonummy sed laoreet magna aliquam dolore erat. euismod erat diam aliquam nonummy aliquam sit ipsum. aliquam sed sed sed sed dolor adipiscing amet.

  • Comparable Materials

    *See Terms of Use Below

Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
20 to 25°C
25°C Recommended
60°C Alternate Cure Schedule
Cure Time Test Methods
Cure Time Test Method
1,440 min Recommended
180 min Alternate Cure Schedule
Viscosity Test Methods
Viscosity Test Method Temperature
Low
10,000 cPs Uncured, Brookfield - RVF, Spindle 4, speed 10 rpm 25°C
Work / Pot Time Test Methods
Work / Pot Time Test Method Temperature
60 min Uncured, 200 g mass 25°C
58 min Uncured, 500 g mass 25°C
47 min Uncured, 1000 g mass 25°C
Linear Shrinkage Test Methods
Linear Shrinkage Test Method
0.01 % Cured
Tensile Strength Test Methods
Tensile Strength Test Method
1,400 psi Cured
Compressive Strength Test Methods
Compressive Strength Test Method
14,000 psi Cured
Impact Strength Test Methods
Impact Strength Type Test Method
0.3 (ft-lb/in) Izod Impact Strength Cured
Dielectric Constant Test Methods
Dielectric Constant Temperature Test Method
5.70 25°C Cured, 100 Hz
20.00 105°C Cured, 100 Hz
4.90 25°C Cured, 1 KHz
11.00 105°C Cured, 1 KHz
4.40 25°C Cured, 10 KHz
8.60 105°C Cured, 10 KHz
Dielectric Strength Test Methods
Dielectric Strength Test Method
1,100 V/mil Cured
Dissipation Factor Test Methods
Dissipation Factor Temperature Test Method
0.12000 25°C Cured, 100 Hz
4.36000 105°C Cured, 100 Hz
0.00700 25°C Cured, 1 KHz
0.97400 105°C Cured, 1 KHz
0.06300 25°C Cured, 100 KHz
0.10400 105°C Cured, 100 KHz
Filler Test Methods
Filler Concentration % Part A Concentration % Part B Concentration Test Method
Non-abrasive filler 50 % 55 % Uncured
Filler Concentration % Test Methods
Filler Concentration % Part A Part B Filler Concentration Test Method
52 % 50 % 55 % Uncured
Surface Resistivity Test Methods
Surface Resistivity Temperature Test Method
1e14 (ohm) 25°C Cured
2e11 (ohm) 105°C Cured
Thermal Conductivity Test Methods
Thermal Conductivity Test Method
0.29 W/m°K Cured
Volume Resistivity Test Methods
Volume Resistivity Temp (°C) Test Method
2e13 (ohms/cm) 25°C Cured
4e9 (ohms/cm) 105°C Cured
Elongation Test Methods
Elongation Test Method
45 % Cured
Shore D Hardness Test Methods
Shore D Hardness Shore Hardness Test Method
75 Cured
Coefficient of Thermal Expansion (CTE) Test Methods
Coefficient of Thermal Expansion (CTE) CTE Test Method
74 (ppm/°C) Cured, Below Tg
180 (ppm/°C) Cured, Above Tg
Density Test Methods
Density Temperature Test Method
1.83 g/cm³ 25°C Uncured
Glass Transition Temp (Tg) Test Methods
Glass Transition Temp (Tg) Glass Transition Temperature (Tg) Test Method
36°C Cured
Specific Gravity Test Methods
Specific Gravity Test Method
2 Cured